Paper Substrate Solvent Based Silicone Release Coating Sf-Src802

• Customization: Available
• CAS No.: Na
• Color: Colorless
• Model NO.: SF-SRC802
• Appearance: Liquid
• Viscosity: 8000-20000
• Use: Silicone Release Coating
• Certificate: ISO
• Solid Content: 32%
• Application: Labels, Baking Paper, Self-Adhesive Envelope
• Substrates: Pet\PE\PC\PP
• Transport Package: 200kg, 1000kg
• Specification: by Sea, Air, Train
• Origin: China
• HS Code: 391000
• Production Capacity: 10000

Product Description

Product Description

SF-SRC802 is a solvent-based, low-peel strength silicone pressure-sensitive adhesive release agent with the characteristics of low migration, fast curing, and stable peeling force. SF-SRC802 silicone polymer has low viscous flow activation energy and good coating performance, and can be coated on the substrate into an extremely thin release coating.
 

Product Parameters

No	Item	Unit	Standard	Method
1	Appearance	/	Colorless transparent liquid	Visual
2	Solid Content	%	32	GB/T 1725
3	Viscosity	mPa·s	8000-20000	GB/T10247
4	Density	g/cm^3	0.91-0.97	GB/T 4472
5	Refractive Index	/	1.41	GB/T 6488

Note: Substrate: 50μmPET film (Corona treatment)   Glue coating thickness: 5±2μm
 

Main Applications

This product is mainly used for labels, baking paper, self-adhesive envelopes, sanitary products, etc., and can be applied to substrates such as PET\PE\PC\PP.


Recommended usage ratio
    The silicone release agent needs to be used in conjunction with a crosslinker, an anchoring agent, and a catalyst. Under the catalytic action of the catalyst, the crosslinker reacts with the main rubber material to solidify into a film, while the anchoring agent mainly adjusts the bonding strength between the film and the substrate. The recommended usage ratio is as follows:

SF-SRC802	CrosslinkerXL38	Anchoring agent M7	Catalyst Pt5000
100	0.8-0.9	0.3-0.7	0.9-1.2

      A large amount of cross-linking agent can prevent glue overflow for thick films, but if it is excessive, it may cause excessive cross-linking, high film hardness, and reduced initial adhesion; to a certain extent, reducing the cross-linking agent can appropriately increase the peeling force, but too low may cause low colloid strength.
A large amount of anchoring agent is helpful for the adhesion of the film, but if it is excessive, there is a risk of small molecules precipitating.
A large amount of catalyst can reduce the curing temperature and increase the curing speed, but if it is excessive, it may cause the film to become harder, shorten the usable time, and increase the cost.

Technology
Glue preparation: According to the predetermined ratio, first add SF-SRC802 to the mixing barrel, then add the diluent (generally diluted to a solid content of 25-35%), stir for 20-40 minutes, and after fully mixing, add the crosslinker XL38 and stir for 3-5 minutes; then add the anchoring agent M7 and stir for 3-5 minutes; finally add the catalyst Pt5000, stir evenly (generally about 30 minutes) and then apply. The diluent can be adjusted according to the specific situation.
Laboratory coating process: Bake for 1-2 minutes at 150ºC.
Production coating process: The oven temperature is set to 120-160ºC, and the baking time and temperature are adjusted according to the coating amount. When the coating film thickness is 10um, the baking time of the glue should be controlled at 60-90s. If the amount of catalyst added is large, the baking time and temperature will be reduced accordingly, but it may have a slight impact on the hardness and cost of the film. Please adjust according to the specific equipment and process.
Typical coating and curing conditions: When the coating film thickness is 20um, the production line speed can be controlled at 10-16m/min, the oven temperature is set from 100ºC to 160ºC and then to 100ºC, and the oven length is 24 meters.

Usage and precautions
    There are volatile solvents in the rubber compound. When using it, be sure to ensure that the environment is well ventilated and away from fire and high temperature; Wear protective equipment during use to avoid contact with the skin. Once contact with the skin, it should be rinsed with soap and running water in time; Coating must be carried out in a suitable environment. It is recommended that the operation room be dust-free, the temperature be controlled at 25-35ºC, and the humidity be controlled at 15-60%. Too much dust will cause particle stains on the finished coating and increase the defective rate. Too low temperature will cause poor leveling and reduced adhesion. Too high humidity can easily cause shrinkage holes in the coating film, and too low humidity can easily cause static electricity safety hazards and cause whitening on the surface.

 

Packaging & Shipping

Transportation

Our Recommendation

Item	Chemical Name	CAS No.	Category
PMS-3S	Octaphenylcyclotetrasiloxane;OTPCS.	546-56-5	Siloxanes& Silazanes
SF-SH73	1,1,1,3,5,5,5-Heptamethyltrisiloxane	1873-88-7	Siloxanes& Silazanes
SF-SO83	Octamethyltrisiloxane	107-51-7	Siloxanes& Silazanes
SF-HF200	Poly(3,3,3-trifluoropropylmethylsiloxane)	63148-56-1	Siloxanes& Silazanes
SF-FP200	D3F; 1,3,5-Tris[(3,3,3-trifluoropropyl)methyl]cyclotrisiloxane	2374-14-3	Siloxanes& Silazanes
SF-QT200	Silanol fluid	70131-67-8	Silicone fluid
SF-VQ200	Vinyl hydroxy silicone oil	67923-19-7	Silicone fluid
SF-BQ200	Benzyl hydroxy silicone oil	80801-30-5	Silicone fluid
SF-PQ200	Diphenylhydroxy silicone oil	68951-93-9	Silicone fluid
SF-MT200	Methoxy-terminated polydimethylsiloxane	68951-97-3	Silicone fluid
SF-MP200	Methyl phenyl silicone oil	63148-58-3	Silicone fluid
SF-BP200	Benzyl silicone oil	63148-52-7	Silicone fluid
SF-DP200	Diphenyl silicone oil	68083-14-7	Silicone fluid
SF-MH200	Methyl hydrogen silicone oil	63148-57-2	Silicone fluid
SF-LH200	Low hydrogen silicone oil	68037-59-2	Silicone fluid
SF-HT200	Hydrogen terminated silicone oil	70900-21-9	Silicone fluid
SF-HT201	Hydrogen-terminated hydrogenated silicone oil	69013-23-6	Silicone fluid
SF-HF200	Hydroxyfluorosilicone oil	63148-56-1	Silicone fluid
SF-MF200	Methyl fluorosilicone oil	/	Silicone fluid
SF-FP200	Fluorosilicone fluid	2374-14-3	Silicone fluid